3M 9082
Harmonization Code : 3907.30.00.40 | Epoxy Mold Compounds containing by weight more than 70 % silicon dioxide
Main features
- 177 deg C Long-Term Bonding
- Low-Outgassing Electronics Adhesion
- Thin 0.05 mm Transfer Layer
Product Description
3M Ultra High Temperature Adhesive Transfer Tape 9082 is a clear 0.05 mm acrylic adhesive transfer tape with a 0.08 mm 55# densified-kraft release liner for thin, high-temperature bonding in electronics and automotive assemblies. The low-outgassing adhesive system retains measurable adhesion through elevated-temperature testing: 180 deg peel adhesion is 8.8 N/cm at 23 deg C and 5.3 N/cm at 177 deg C on aluminum-foil-backed specimens. Long-term temperature resistance is 177 deg C and short-term resistance is 280 deg C. The construction is intended for assemblies that combine thin bondlines with elevated processing or operating temperatures.
Key features
- High-temperature acrylic bonding: Long-term temperature resistance reaches 177 deg C, with short-term exposure resistance to 280 deg C.
- Low-outgassing thin transfer layer: The clear 0.05 mm adhesive layer provides a thin bonding profile for electronics and automotive assemblies.
- Measured elevated-temperature adhesion: Peel adhesion remains measurable through 230 deg C testing, with 5.3 N/cm recorded at 177 deg C.
Applications
Applications include automotive under-hood bonding, flexible printed circuit and FR-4 attachment, electronics and heat-sink bonding, and solder-reflow process assemblies.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Other Properties
Thermal Properties
Additional Information
As-supplied / before-processing properties
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Color | Clear | As supplied | |
| Density | 0.98 | g/cm^3 | Typical |
| Adhesive type | Acrylic adhesive system | High-temperature adhesive | |
| Adhesive thickness | 0.05 | mm | ASTM D3652; typical |
| Liner | 55# densified kraft | White with green 3M print | |
| Liner thickness | 0.08 | mm | Typical |
After-processing / final-state properties
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| 180 deg peel adhesion at 23 deg C | 8.8 | N/cm | ASTM D3330; 2 mil aluminum foil backing; typical |
| 180 deg peel adhesion at 177 deg C | 5.3 | N/cm | ASTM D3330; specimen conditioned 2 min at temperature; typical |
| Overlap shear strength at 23 deg C | 620 | kPa | ASTM D1002 / ISO 4587; stainless steel; typical |
| Long-term temperature resistance | 177 | deg C | Days to weeks; typical |
| Short-term temperature resistance | 280 | deg C | Minutes to hour; typical |
| Dielectric strength at 23 deg C | 1200 | V | ASTM D149; typical |